Repower® RE10TX

Repower RE10TX – one-component structural repair material based on cement, containing polymer and fibres.
Conforms to EN 1504-3 / class R2

Can be used on horizontal and vertical surfaces
In the repair of reinforced concrete structures
In protecting concrete from the effects of sulfates and chlorine
In the repair and protection of marine structures
In the repair and protection of underground historical monuments
In repair and restoration of rough concrete surfaces with high strength
In the repair of precast concrete elements
In the repair of special coatings and surfaces with light and medium traffic loads
For filling gaps in the connecting elements of forms

Click to order the product faster

Repower RE10TX – one-component structural repair material based on cement, containing polymer and fibres.
Conforms to EN 1504-3 / class R2

Can be used on horizontal and vertical surfaces
In the repair of reinforced concrete structures
In protecting concrete from the effects of sulfates and chlorine
In the repair and protection of marine structures
In the repair and protection of underground historical monuments
In repair and restoration of rough concrete surfaces with high strength
In the repair of precast concrete elements
In the repair of special coatings and surfaces with light and medium traffic loads
For filling gaps in the connecting elements of forms

Product composition	Cement, mineral fillers and special chemical additives
Color	Grey
Pressure resistance - EN 12190 After 7 days	≥ 50 MPa
Pressure resistance - EN 12190 After 28 days	≥ 60 MPa
Bond strength to concrete EN 1542	≥ 2 MPa
Modulus of elasticity EN 13412 (28 days)	≥ 20 GPa
Bending resistance EN 196-1 (28 days)	≥ ≥ 9 N/mm ²
Capillary water absorption - EN 13057	≤ 0.5 kg.m ^-2 .h ^-0.5
Chloride ion count EN 1015-17	≤ 0,05%
Resistance to carbonation EN 13295	dk ≤ control concrete (MC(0.45))
Application thickness (one layer)	min. 10 mm, max. 40 mm
Temperature of the treated surface	+5°C +30°C
Operating temperature	-20°C +400°C
Application time	45 min.
Possibility of movement on the surface	In 24 hours
Time for complete hardening	In 28 days
Density of the mixture	2.25 kg/l